Anodized electroplated aluminum structures

ABSTRACT

Anodized electroplated aluminum structures and methods for making the same are disclosed. Cosmetic structures according to embodiments of the invention are provided by electroplating a non-cosmetic structure with aluminum and then anodizing the electroplated aluminum. This produces cosmetic structures that may possess desired structural and cosmetic properties and that may be suitable for use as housing or support members of electronic devices.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a division of U.S. application Ser. No. 13/414,542,filed Mar. 7, 2012, entitled “ANODIZED ELECTROPLATED ALUMINUM STRUCTURESAND METHODS FOR MAKING THE SAME”, which claims the benefit of U.S.Provisional Application No. 61/449,855 filed Mar. 7, 2011, entitled“ANODIZED ELECTROPLATED ALUMINUM STRUCTURES AND METHODS FOR MAKING THESAME”, the contents of which are incorporated herein by reference intheir entirety for all purposes.

BACKGROUND

Electronic devices such as computers, cellphones, and portable mediadevices are often manufactured to exhibit desired cosmeticcharacteristics. In addition, such devices are manufactured with minimumstructural requirements. It is desirable for certain materials used insuch devices to exhibit sufficient structural integrity and cosmeticappeal. However, these two qualities can oppose each other depending onthe material used. For example, a material may be aestheticallypleasing, but lack the desired structural properties, or alternatively,the material may be structurally sound, but does not exhibit desiredcosmetics.

SUMMARY

Anodized electroplated aluminum structures and methods for making thesame are disclosed.

In some embodiments, a cosmetic structure may include a non-cosmeticstructure having a surface, a qualification layer disposed on thesurface, and an electroplated aluminum layer disposed on thequalification layer. The electroplated aluminum layer may have aninitial applied thickness ranging between 15 micrometers and 120micrometers. The cosmetic structure may also include an aluminumanodized layer integrally formed with the electroplated aluminum layer.

In some embodiments, a method for making a cosmetic structure mayinclude providing a non-cosmetic structure, preparing the non-cosmeticstructure for an electroplating process, and electroplating the preparednon-cosmetic structure with aluminum to provide an electroplatedaluminum structure. The electroplated aluminum layer may have an initialapplied thickness ranging between 15 micrometers and 120 micrometers.The method may also include processing the electroplated aluminumstructure to obtain a predetermined finish. A portion of theelectroplated aluminum may be removed to provide the predeterminedfinish. The method may also include anodizing the processedelectroplated aluminum structure having the predetermined finish toprovide the cosmetic structure.

In some embodiments, an electronic device may include a display, a userinterface, and a housing for securing the display and user interface.The housing may include a metal having an anodized electroplatedaluminum cosmetic finish.

In some embodiments, a cosmetic structure may include a non-cosmeticstructure, and an electroplated aluminum layer disposed on thenon-cosmetic structure. The electroplated aluminum layer may includefirst and second dopants each having a different grain structure. Thecosmetic structure may also include an aluminum anodized layerintegrally formed with the electroplated aluminum layer.

In some embodiments, an article may include an aluminum structure, andan electroplated aluminum layer on the aluminum structure. An oxidelayer of the aluminum structure may be removed.

In some embodiments, a method may include providing an aluminumstructure, and, in a sealed environment, removing an oxide layer fromthe aluminum structure, and, after the removing, electroplating thealuminum structure to form an electroplated aluminum layer on thealuminum structure.

In some embodiments, an article may include a non-cosmetic structure.The non-cosmetic structure may include a first portion of a firstmaterial type, and a second portion of a second material type. Thearticle may also include a first electroplated layer on the firstportion, and a second electroplated layer on the second portion.

In some embodiments, a method may include providing a non-cosmeticstructure. The non-cosmetic structure may include a first portion of afirst material type, and a second portion of a second material type. Themethod may also include electroplating the non-cosmetic structure toform a first electroplated layer on the first portion and a secondelectroplated layer on the second portion.

In some embodiments, an article may include a non-cosmetic structure, afirst electroplated layer on the non-cosmetic structure, a firstanodized layer on the first electroplated layer, a second electroplatedlayer on the first anodized layer, and a second anodized layer on thesecond electroplated layer.

In some embodiments, a method may include providing a non-cosmeticstructure, electroplating the non-cosmetic structure to form a firstelectroplated layer on the non-cosmetic structure, anodizing the firstelectroplated layer to form a first anodized layer on the firstelectroplated layer, processing the anodized electroplated structure toremove a portion of the anodized electroplated structure, electroplatingthe processed anodized electroplated structure to form a secondelectroplated layer, and anodizing the second electroplated layer toform a second anodized layer on the second electroplated layer.

In some embodiments, a method may include providing a non-cosmeticstructure, processing a portion of the non-cosmetic structure, andelectroplating the non-cosmetic structure to form an electroplated layeron an unprocessed portion of the non-cosmetic structure. The processingmay include at least one of masking and laminating the portion. Afterthe electroplating, the method may include surface finishing theelectroplated layer.

BRIEF DESCRIPTION OF THE DRAWINGS

The above and other aspects and advantages of the invention will becomemore apparent upon consideration of the following detailed description,taken in conjunction with accompanying drawings, in which like referencecharacters refer to like parts throughout, and in which:

FIG. 1 shows an illustrative non-cosmetic structure that may receive acosmetic finish in accordance with an embodiment of the invention;

FIG. 2 shows an illustrative cross-sectional view of such a cosmeticstructure in accordance with an embodiment of the invention;

FIG. 3 shows an illustrative process for manufacturing a cosmeticstructure having an anodized electroplated aluminum surface according toan embodiment of the invention;

FIG. 4 shows an illustrative cross-sectional view of a cosmeticstructure with aluminum plated on an aluminum structure in accordancewith an embodiment of the invention;

FIG. 5 shows an illustrative process for manufacturing a cosmeticstructure having an anodized electroplated aluminum surface on analuminum structure in accordance with an embodiment of the invention;

FIG. 6 shows an illustrative cross-sectional view of a surface of atleast one of an electroplated layer and an anodized layer of a cosmeticstructure in accordance with an embodiment of the invention;

FIG. 6A shows an illustrative cross-sectional view of a surface of atleast one of an electroplated layer and an anodized layer of a cosmeticstructure having a particular grains structure in accordance with anembodiment of the invention;

FIG. 6B shows an illustrative cross-sectional view of a surface of atleast one of an electroplated layer and an anodized layer of a cosmeticstructure having a particular grains structure in accordance with anembodiment of the invention;

FIG. 6C shows an illustrative cross-sectional view of a surface of atleast one of an electroplated layer and an anodized layer of a cosmeticstructure having a particular grains structure in accordance with anembodiment of the invention;

FIG. 6D shows an illustrative cross-sectional view of a surface of atleast one of an electroplated layer and an anodized layer of a cosmeticstructure having a particular grains structure in accordance with anembodiment of the invention;

FIG. 7 shows an illustrative cross-sectional view of a selectivelyelectroplated cosmetic structure in accordance with an embodiment of theinvention;

FIG. 8 shows an illustrative process for manufacturing a cosmeticstructure by selective electroplating according to an embodiment of theinvention;

FIG. 9 shows an illustrative cross-sectional view of a cosmeticstructure including multiple substrates in accordance with an embodimentof the invention;

FIG. 10 shows an illustrative process for manufacturing a cosmeticstructure including multiple substrates according to an embodiment ofthe invention;

FIG. 11 shows an illustrative cross-sectional view of a double anodizedcosmetic structure in accordance with an embodiment of the invention;

FIG. 12 shows an illustrative process for manufacturing a cosmeticstructure by double anodization according to an embodiment of theinvention; and

FIG. 13 shows an illustrative process for manufacturing a cosmeticstructure with an electroplated aluminum layer having a minimumthickness according to an embodiment of the invention; and

FIG. 14 is a schematic view of an illustrative electronic device inaccordance with an embodiment of the invention.

DETAILED DESCRIPTION

Cosmetic structures according to embodiments of the invention areprovided by electroplating a non-cosmetic structure and then anodizingthe electroplated structure. This can, for example, produce cosmeticstructures that possess desired structural and cosmetic properties andthat are suitable for use as housing or support members of electronicdevices.

FIG. 1 shows an illustrative non-cosmetic structure 100 that may receivea cosmetic finish in accordance with an embodiment of the invention.Structure 100 may have any suitable size and shape. For example,structure 100 can have curved surfaces, planar surfaces, edges, cutouts,recesses, cavities, through-holes, threaded holes or cavities, or anycombination thereof. As illustrated in FIG. 1, structure 100 can have acombination of curved and planar surfaces, and one or morethrough-holes.

In some embodiments, structure 100 may be used as a part of anelectronic device such as, for example, a portable media player, a smartphone, a laptop computer, or a tablet. Structure 100 may providestructural support for the electronic device and may also be visible toa user. Structural support may be provided in the form of a cover, suchas a backplate, or in the form of a frame (e.g., a shell of a laptopbody). Because portions of structure 100 may be visible to the user, acosmetic finish can be applied in accordance with embodiments of thisinvention.

Structure 100 can be constructed from any suitable material. Forexample, structure 100 can be constructed from steel or a steel alloy,magnesium, aluminum or an aluminum alloy, or titanium. Each of thesemetals in their raw and untreated state, however, do not provide thecombination of durability and desired cosmetic appearance. Steel, forexample, can be polished to exhibit a shiny mirror-like finish, but issusceptible to scratches, which dull the finish, and readily retains oilleft behind by fingerprints. Both magnesium and aluminum exhibitundesired cosmetic appearance—that is, they both have a dull finish.

As another example, structure 100 can be constructed from a polymer, aglass embedded plastic, or materials such as ceramic, nylon, carbonfiber, or any combination of two or more of the foregoing. As yetanother example, structure 100 can be constructed to include both ametal (e.g., steel, magnesium, or aluminum) and a plastic material. Theplastic material may provide a “window” suitable for passage of RFsignals. Further, structure 100 may include an assembly or a singlepart.

Non-cosmetic structures such as structure 100 may be subjected to acosmetic finishing process according to embodiments of the invention toprovide a cosmetic structure. FIG. 2 shows an illustrativecross-sectional view of such a cosmetic structure. As shown, cosmeticstructure 200 can include non-cosmetic structure 210, qualificationlayer 220, electroplated aluminum layer 230, and aluminum anodized layer240. The thickness of each layer is illustrative and it is understoodthat the thickness of each layer may vary. In addition, the thickness ofstructure 210 can also vary.

Non-cosmetic structure 210 can include any suitable structure such asthat described above in connection with structure 100 of FIG. 1. Ifnon-cosmetic structure 210 includes an edge, through-hole, cavity,threaded hole, or any other feature or combination thereof, each oflayers 220, 230, and 240 can exist on each those features. This canensure that each feature of non-cosmetic structure 210 has a desiredcosmetic finish, which provides aesthetics and functional properties.

Qualification layer 220 can include one or more materials that preparenon-cosmetic structure 210 for an aluminum electroplating process. Forexample, qualification layer 220 can include a nickel layer. As anotherexample, qualification layer 220 can include a copper layer and a nickellayer, which may be deposited on top of the copper layer. Layer 220 maybe applied to structure 210 using any suitable process, including, forexample, an immersion bath, electroplating, electroless plating,sputtering, or physical vapor deposition (PVD).

Qualification layer 220 can serve as a bonding surface for electroplatedaluminum layer 230, and as such layer 230 can follow the contours andplacement of layer 220. Because layer 230 may mimic placement of layer220, it is desirable for layer 230 to be deposited on non-cosmeticstructure 210 such that it forms a uniform coating of a predeterminedthickness. The thickness may range between 5 um and 20 um, and in someembodiments may be about 10 um. Although it is desirable to have auniform thickness, it is understood that the thickness of layer 220 mayvary throughout. For example, layer 220 may vary in thickness by a fewmicrons. In addition, it is further understood that the thickness oflayer 220 may vary (e.g., from 10 um to 20 um) depending on the featurebeing coated. For example, the thickness of layer 220 on a relativelylarge planer surface may be greater than the thickness of layer 220 on acavity or threaded insert.

The uniformity of the coating of layer 220 may be such that no orsubstantially no gaps or pores exist that will expose non-cosmeticstructure 210. A uniform coating of layer 220 can ensure thatelectroplated aluminum layer 230 is continuously distributed acrossstructure 210.

Electroplated aluminum layer 230 is a layer of aluminum or alloy thereofthat is electroplated on top of qualification layer 220. Electroplatingis a plating process in which metal ions in a solution are moved by anelectric field to coat an electrode. The solution may include anelectrolytic bath of toluene or ionic liquid from which an aluminum saltcan be reduced. The electrode may be the combination of structure 210and layer 220. The process can be regulated by controlling a variety ofparameters, including voltage, amperage, temperature, dwell time, andpurity of solution. It should be appreciated that parameters of theelectroplating process may be adjusted depending on physicalcharacteristics (e.g., shape) of structure 210. For example, layer 230may be thicker at edges of structure 210. As another example, curvedportions of structure 210 may be plated with aluminum or aluminum alloyin a manner that compensates for the curves.

Aluminum electroplated layer 230 can have any suitable thickness. Forexample, the thickness of layer 230 can vary between 10 and 120 microns,between 10 um and 75 um, 18 um and 25 um. In some embodiments, thethickness can be 10 microns, 18 microns, 33 microns, 50 microns, or 75microns. It may be desirable that layer 230 not exceed a maximumthickness to prevent variability in the surface. It may also bedesirable for layer 230 to have at least a minimum thickness toaccommodate a processing step that removes a portion of layer 230 beforeit is anodized and to ensure structural reliability of layer 230. Theprocessing step may remove any suitable amount of layer 230 to achievedesired results (e.g., a matte or mirror surface). The processing stepmay blast away or etch away a portion of layer 230 to provide a mattesurface. It should be appreciated that parameters of the surfacefinishing process may be adjusted depending on physical characteristics(e.g., shape) of structure 210. For example, an amount of layer 230being removed from a planar surface may be different from an amount oflayer 230 being removed from sharp curves or edges. In addition, oralternatively, the processing step can lathe or polish away a portion oflayer 230 to provide a mirror finish.

In some embodiments, a minimum thickness of 10 um of layer 230 may betoo thin to polish, but may be suitable for obtaining a textured ormatte finish. As another example, a minimum thickness of 18 um of layer230 may be required to achieve a mirror finish. It should be appreciatedthat the minimum thickness of layer 230 required for achieving any ofthe textured or mirror finish may depend on the material selected instructure 210. For example, the thickness of the electroplated aluminumlayer may be based on a stiffness of the non-cosmetic structure. Asanother example, a glass substrate may require a thicker layer 230 thana steel substrate in order to prevent cracking.

Electroplating with aluminum, rather than with other materials, canprovide certain benefits for a finished part, including, but not limitedto, cosmetic appeal, desired thermal qualities, structural reliability,and flexibility during manufacturing, and corrosion resistance. Inaddition, the soft property of aluminum can be leveraged duringmanufacturing (e.g., laser marking/etching and/or machining can beperformed on an aluminum plated part), work hardened materials can beplated with aluminum, and a non-cosmetic part may even be colored firstprior to being plated with aluminum.

Anodized aluminum layer 240 may be a layer wherein a surface portion ofelectroplated aluminum layer 230 is anodized. Anodizing can increasecorrosion resistance and surface hardness (e.g., to prevent scratching)of aluminum layer 230. In addition, anodizing can permit coloring ofaluminum layer 230. Anodized aluminum layer 240 can have any suitablethickness. In some embodiments, layer 230 can be anodized via directelectrical current (DC) or via pulses of current (e.g., pulseanodization), where layer 230 may be bathed (e.g., in sulfuric acid) toconvert at least a portion of the surface of layer 230 into aluminumoxide. In some embodiments, the thickness of the aluminum oxide layermay be 35 microns or less. For example, the thickness can be about 10microns. In other embodiments, the thickness can range between 5 and 35microns, 10 and 30 microns, and 10 and 20 microns. Therefore, layer 230may need to have an initial thickness greater than the desired thicknessof layer 240, so that sufficient electroplated aluminum is available forconversion.

It should also be appreciated that, because the anodization process mayresult in a cloudy aluminum oxide layer, steps can be taken to improvethe clarity thereof. For example, if pulse anodization is employed, thepulses of current can be adjusted to achieve improved clarity. Inaddition, additional processing steps (e.g., polishing and texturing)may be also applied to layer 240.

FIG. 3 shows an illustrative process 300 for manufacturing a cosmeticstructure having an anodized electroplated aluminum surface according toan embodiment of the invention. Beginning at step 310, a non-cosmeticstructure (e.g., non-cosmetic structure 210) can be provided. Thenon-cosmetic structure can be any suitable shape or construction and canbe constructed from a metal, a plastic, or combination thereof. Seediscussion of structure 100 above for additional details for suitablenon-cosmetic structures.

At step 320, the non-cosmetic structure may be processed or prepared foran electroplating step. In some embodiments, certain parts or portionsof the non-cosmetic structure can be masked so that the masked portionwill not be cosmetically finished. The non-cosmetic structure may beprepared by being cleaned (e.g., to remove impurities, grease, or anyoxidation buildup). The non-cosmetic structure can also be prepared byreceiving a qualification layer. If desired, the non-cosmetic structurecan be polished or textured prior to or after the cleaning step. Thequalification layer, as discussed above in connection with FIG. 2, mayinclude a nickel layer or a copper layer that is then covered by anickel layer. For example, the nickel layer may have a particularoptical characteristic (e.g., a particular brightness). As alsodiscussed above, qualification layer may uniformly coat all desiredfeatures of the non-cosmetic structure. If desired, the qualificationlayer can also be polished, textured, or subjected to one or more rinsesolvents. In some embodiments, the qualification layer may further bemasked with any suitable material.

At step 330, the processed non-cosmetic structure may be electroplatedwith aluminum. In some embodiments, the electroplating step may includethe use of toluene, ionic liquid, aluminum sulphite/sulphate, and/or anyother suitable material. After an electroplated aluminum layer ofdesired thickness is deposited onto the non-cosmetic structure, theprocess may proceed to step 340. At step 340, the electroplated aluminumlayer may be processed to attain a desired finish. Depending on how theelectroplated aluminum layer is processed, it can exhibit, for example,a mirror-like finish or a matte finish.

In some embodiments, the electroplated aluminum layer may first betextured by a blasting and/or an etching process (e.g., laser etching),and subsequently surface finished. Surface finishing may, for example,involve localized processing of the electroplated aluminum layer using atargeted or targeting process. Any of a blast process, etching (e.g.,laser etching), a physical mask, and/or any other suitable finishingprocess may be applied as part of surface finishing the electroplatedaluminum layer.

At step 350, the processed electroplated aluminum structure may beanodized. The anodizing step can optionally include any of dye coloringand sealing. Sealing may include the use of any suitable material thatmay allow for the anodized layer to be further electroplated and/oranodized, if desired. In embodiments that include dye coloring andsealing, for example, a subsequent surface finish may also be performedon any visible or non-visible portion of the anodized electroplatedaluminum layer. Such surface finishing of the anodized layer may, forexample, include polishing, etching (e.g., of graphics and/or ofartwork), engraving, CNC milling, and/or drilling microperforationstherein. Following step 350, an anodized electroplated aluminumstructure with appealing cosmetics and functional properties may beprovided, and any other components may be attached to the cosmeticstructure to form at least a part of an assembly.

One or more of the steps 310, 320, 330, 340, and 350 may be performed byautomated machinery in a controlled environment devoid of oxygen. Forexample, the steps may be performed in a nitrogen only atmosphere. It isunderstood that additional steps may be added without departing from thespirit of the invention. For example, a cleaning step may be added afterthe completion of step 330. As another example, an additional aluminumcoating step may be used to coat the non-cosmetic structure withaluminum. The additional aluminum coating step may be implemented byphysical vapor deposition, thermal spray, or cold spray. This coatingstep may be applied before or after the electroplating step.

In some embodiments, an aluminum or aluminum alloy substrate orstructure can be electroplated with aluminum or aluminum alloy. FIG. 4shows an illustrative cross-sectional view of a cosmetic structure withaluminum plated on an aluminum structure in accordance with anembodiment of the invention. Similar to cosmetic structure 200 of FIG.2, cosmetic structure 400 can include non-cosmetic aluminum structure410, electroplated aluminum layer 420, and anodized layer 430. However,cosmetic structure 400 may lack a qualification layer (e.g., layer 220of FIG. 2). In some embodiments, to overcome potential difficulties inachieving aluminum plating on an aluminum substrate, an existing oxidelayer on the aluminum substrate may first be removed (e.g., preferablyin a sealed environment devoid of oxygen) prior to plating the aluminumstructure with aluminum. With an existing oxide layer removed, aluminummay then be electroplated much more easily onto the aluminum structure.This can result in decreased manufacturing costs (e.g., a qualificationlayer is no longer required) and can maintain structural integrity of afinished cosmetic structure (e.g., any corrosion of a qualificationlayer can be avoided).

FIG. 5 shows an illustrative process for manufacturing a cosmeticstructure having an anodized electroplated aluminum surface on analuminum structure. Process 500 may begin at step 502. At step 504, anon-cosmetic aluminum structure (e.g., structure 410) may be provided.

At step 506, an existing oxide layer (not shown) on the non-cosmeticaluminum structure may be removed. Any suitable chemical process may beapplied to the surface of the non-cosmetic aluminum structure, forexample, to remove any oxide layer that may be present. At step 508,after the oxide layer is removed from the non-cosmetic aluminumstructure, the non-cosmetic aluminum structure may be electroplated withaluminum. As discussed above in connection with FIG. 2, it should beappreciated that any parameters of the electroplating process (e.g.,voltage, current, temperature, and dwell time) can be controlled toproduce a desired thickness and quality of the electroplated aluminumlayer. In some embodiments, a finishing process can be performedimmediately after step 508 to attain a desired finish for theelectroplated aluminum layer (e.g., layer 420). For example, dependingon how the electroplated aluminum layer is processed, it can exhibit amirror like finish or a matte finish.

Though not shown, after step 508, the electroplated aluminum structuremay be anodized. In some embodiments, a dye coloring process can beperformed during the anodizing in order to achieve a coloring effect.Following the anodizing, a cosmetic structure having an anodizedelectroplated aluminum surface on an aluminum structure may be provided.

In some embodiments, the hardness of an electroplated layer (e.g., layer420) can be controlled. For example, electroplating of a non-cosmeticstructure may include immersing the non-cosmetic structure in a firstbath of aluminum or aluminum alloy solution having a particular grainstructure (or size), and subsequently immersing the electroplatednon-cosmetic structure in a second bath of aluminum or aluminum alloysolution having a different grain structure (or size). As anotherexample, the non-cosmetic structure may be immersed in a bath ofaluminum or aluminum alloy solution having a mixed grain structure (ormixed grain sizes). In particular, the mixed grain structure (or sizes)may be produced by mixing a first aluminum or aluminum alloy solutionhaving a particular grain structure (or size) with a second solution(e.g., of aluminum or of any other suitable type of element) having adifferent grain structure (or size). In this manner, one or moreproperties of an electroplated layer's surface can be modified (e.g.,chemically) to provide a desired structural integrity. In someembodiments, the aluminum or aluminum alloy solution to be electroplatedmay be modified with one or more dopants to produce a hardness qualityof grains. It should be appreciated that any suitable type of materialmay be used to dope the aluminum or aluminum alloy solution, as long asa resulting electroplated layer exhibits a desired hardness quality. Insome embodiments, 99.99% pure aluminum may be used for theelectroplating, which may allow for better control of the thickness ofthe grain structure. For example, various aluminum and dopant baths maybe mixed in any suitable manner and used in electroplating to controlthe thickness of the grain structure of a resulting electroplated layer.FIG. 6 shows an illustrative cross-sectional view 600 of a surface of atleast one of an electroplated layer of a cosmetic structure inaccordance with an embodiment of the invention. Layer 610 can includesurface 620, which can include a pattern of grains 630 that at leastpartially defines a structural characteristic of layer 610.

FIG. 6A shows an illustrative cross-sectional view of a surface of atleast one of an electroplated layer and an anodized layer of a cosmeticstructure having a particular grains structure in accordance with anembodiment of the invention. Surface 620 a of cosmetic structure 600 acan include a pattern of grains 630 a having a relatively large or roughgrain structure. FIG. 6B shows an illustrative cross-sectional view of asurface of at least one of an electroplated layer and an anodized layerof a cosmetic structure having a particular grains structure inaccordance with an embodiment of the invention. Surface 620 b ofcosmetic structure 600 b can include a pattern of grains 630 b having arelatively small or fine grain structure, in contrast to pattern ofgrains 630 a.

In some embodiments, the electroplated layer and/or the anodized layermay be controlled to include layered patterns of grains each havingrelatively different grain structures. FIG. 6C shows an illustrativecross-sectional view of a surface of at least one of an electroplatedlayer and an anodized layer of a cosmetic structure having a particulargrains structure in accordance with an embodiment of the invention.Surface 620 c of cosmetic structure 600 c can include a lower pattern ofgrains 630 c having a relatively large or rough grain structure and anupper pattern of grains 632 c having a relatively small or fine grainstructure. FIG. 6D shows an illustrative cross-sectional view of asurface of at least one of an electroplated layer and an anodized layerof a cosmetic structure having a particular grains structure inaccordance with an embodiment of the invention. Surface 620 d ofcosmetic structure 600 d can include a lower pattern of grains 630 dhaving a relatively small or fine grain structure and an upper patternof grains 632 d having a relatively large or rough grain structure, incontrast to layer 610.

In some embodiments, a non-cosmetic structure may be selectivelyelectroplated to provide a selectively plated cosmetic structure. Thiscan yield a desired cosmetic appearance on select portions of anon-cosmetic structure. FIG. 7 shows an illustrative cross-sectionalview of a selectively electroplated cosmetic structure in accordancewith an embodiment of the invention. Cosmetic structure 700 may includenon-cosmetic structure 710, non-plated portions 720, electroplatedportion 730, and electroplated layer 740. Though not shown, in someembodiments, cosmetic structure 700 may also include a qualificationlayer similar to layer 220 of cosmetic structure 200. In addition, itshould be appreciated that cosmetic structure 700 may further include ananodized layer (e.g., similar to layer 240 of FIG. 2).

FIG. 8 shows an illustrative process for manufacturing a cosmeticstructure by selective electroplating according to an embodiment of theinvention. Process 800 may begin at step 802. At step 804, anon-cosmetic structure (e.g., structure 710) may be provided. At step806, portions of the non-cosmetic structure that are not to beelectroplated (e.g., non-plated portions 720) may be masked orlaminated. It should be appreciated that masking or lamination of thenon-cosmetic structure may be achieved using any suitable type ofmaterial. At step 808, the masked or laminated non-cosmetic structuremay be electroplated (e.g., with aluminum or any suitable type ofmaterial). With portions of the non-cosmetic structure being masked orlaminated, only uncovered portion(s) (e.g., electroplated portion 730)of the structure may be electroplated at step 808. Though not shown, themask or laminating material may be removed at any time afterelectroplating is complete of the uncovered portion(s) is complete.

In some embodiments, a non-cosmetic structure may include two or moretypes of material, where a different finish on each type of material maybe desired. FIG. 9 shows an illustrative cross-sectional view of acosmetic structure including multiple substrates in accordance with anembodiment of the invention. Cosmetic structure 900 may includenon-cosmetic structure 910, which may be constructed of structuralportions 920 of one material type (e.g., aluminum) and a structuralportion 930 of another material type (e.g., ceramic), and electroplatedlayer 940. Electroplated layer 940 may include first finished portions950 overlaid on structural portions 920, and a second finished portion960 overlaid on structural portion 930. Though not shown, in someembodiments, cosmetic structure 900 may also include a qualificationlayer similar to layer 220 of cosmetic structure 200.

FIG. 10 shows an illustrative process for manufacturing a cosmeticstructure including multiple substrates according to an embodiment ofthe invention. Process 1000 may begin at step 1002. At step 1004, anon-cosmetic structure (e.g., non-cosmetic structure 910) may beprovided. The non-cosmetic structure may include one or more structuralportions of one material type (e.g., structural portions 920) and one ormore portions of another material type (e.g., structural portion 930).

At step 1006, the non-cosmetic structure may be electroplated to form anelectroplated layer. Depending on properties of the non-cosmeticstructure that is directly beneath the electroplated layer, one portionof the electroplated layer may have properties that are different fromthose of another portion of the electroplated layer. In someembodiments, after step 1006, the electroplated layer may be surfacefinished. Due to the different material properties of the differentportions of the non-cosmetic structure, a characteristic of one or moreportions of an electroplated layer (e.g., first finished portions 950)that is deposited on the one or more structural portions of one materialtype (e.g., structural portions 920) may be different from acharacteristic of one or more portions of the electroplated layer (e.g.,second finished portion 960) that is deposited on the one or more of thestructural portions of another material type (e.g., structural portion930). For example, if the non-cosmetic structure includes one or morealuminum portions and one or more ceramic portions, surface finishing anelectroplated layer may result in a portion of the electroplated layerdeposited on the aluminum portions to exhibit a matte finish, and aportion of the electroplated layer deposited on the ceramic portions toexhibit a clear finish.

In some embodiments, a non-cosmetic structure may be plated and anodizedmore than once (e.g., two times) to provide a finished cosmeticstructure that may include a desired pattern of surface texture and/orcolors. For example, a non-cosmetic structure may be electroplated(e.g., with aluminum) to form a first electroplated layer. The firstelectroplated layer may then be anodized to form a first anodized layerover the first electroplated layer, and a portion of the firstelectroplated layer and a portion of the first anodized layer may eachbe removed. As a result, a recess may be created between remainingportions of the first electroplated layer and the first anodized layer,and a second electroplated layer may be formed in the recess. A secondanodized layer may then be formed over the second electroplated layer,resulting in a double anodized cosmetic structure. Such a doubleanodization process may eliminate any need to mask portions of thenon-cosmetic structure during manufacturing. FIG. 11 shows anillustrative cross-sectional view of a double anodized cosmeticstructure in accordance with an embodiment of the invention. Cosmeticstructure 1100 may include non-cosmetic structure 1110, firstelectroplated layer portions 1120 (e.g., of aluminum), first anodizedlayer portions 1130, second electroplated layer portion 1150, and secondanodized layer portion 1160. Though not shown, in some embodiments,cosmetic structure 1100 may also include one or more qualificationlayers similar to layer 220 of cosmetic structure 200. Though cosmeticstructure 1100 is shown to have a particular pattern of electroplatedand anodized layers, it should be appreciated that any suitable designor pattern of each of these layers may be achieved with doubleanodization.

FIG. 12 shows an illustrative process for manufacturing a cosmeticstructure by double anodization according to an embodiment of theinvention. Process 1200 may begin at step 1202. At step 1204, anon-cosmetic structure (e.g., non-cosmetic structure 1110) may beprovided.

At step 1206, the non-cosmetic structure may be electroplated (e.g.,with aluminum) to form an electroplated layer (e.g., including firstelectroplated layer portions 1120 and one or more other firstelectroplated layer portions that are not shown). In some embodiments, afinishing process can be performed immediately after step 1206 to attaina desired finish of the electroplated layer. For example, depending onhow the electroplated aluminum layer is processed, it can exhibit amirror like finish or a matte finish.

At step 1208, the electroplated structure may be anodized to form ananodized layer (e.g., first anodized layer portions 1130 and one or moreother first anodized layer portions that are not shown). In someembodiments, a dye coloring process can be performed during anodizingstep 1208 in order to achieve a coloring effect.

At step 1210, the anodized electroplated structure may be processed toremove a portion of the anodized electroplated structure. As a result,what remains of the anodized electroplated structure may function as amask for use during further steps of the manufacturing of the cosmeticstructure. The modification can include, for example, cutting (e.g., vialaser etching) one or more portions of the first anodized layer (e.g.,first anodized layer portions (not shown) other than first anodizedlayer portions 1130) and electroplated layer (e.g., first electroplatedlayer portions (not shown) other than first electroplated layer portions1120) to create one or more recesses (not shown, but may be at leastpartially occupied by second electroplated layer portion 1150 and secondanodized layer portion 1160).

At step 1212, the modified anodized electroplated structure may befurther electroplated to form one or more second electroplated layers(e.g. electroplated layer portion 1150). This second electroplated layermay be processed to attain a desired finish. At step 1214, a secondanodization process may be performed on the second electroplatedstructure. Anodizing step 1214 may optionally include dye coloring.Following step 1214, a double anodized electroplated structure withappealing cosmetics and functional properties may be provided.

In some embodiments, a dye coloring process performed during the firstanodizing step 1206 may employ a dye color different from that employedin a dye coloring process performed during the second anodizing step1212. It should be appreciated that step 1210 can be performed at anytime after step 1206 (e.g., prior to surface finishing the electroplatedlayer). Further, the first electroplated layer may be formed from amaterial that is different from a material that forms the secondelectroplated layer. For example, the first electroplated layer may beformed from aluminum, whereas the second electroplated layer may beformed from nickel.

FIG. 13 shows an illustrative process for manufacturing a cosmeticstructure with an electroplated aluminum layer having a minimumthickness according to an embodiment of the invention. Process 1300 maybegin at step 1302. At step 1304, a non-cosmetic structure (e.g.,non-cosmetic structure 210) may be provided.

At step 1306, the non-cosmetic structure may be electroplated withaluminum. As discussed above in connection with FIG. 2, it may bedesirable for an electroplated aluminum layer to have a minimumthickness to accommodate a processing step that removes a portion of theelectroplated aluminum layer before it is anodized and to ensurestructural reliability. Thus, the electroplating of step 1306 mayinclude electroplating the non-cosmetic structure such that theelectroplated aluminum layer has a minimum thickness. As discussed abovein connection with FIG. 2, it should be appreciated that the minimumthickness of the electroplated aluminum layer required for achieving anyof the textured or mirror finish may depend on a type of material of thenon-cosmetic structure. For example, the thickness of the electroplatedaluminum layer may be based on a stiffness of the non-cosmeticstructure. As another example, a glass substrate may require a thickerlayer 230 than a steel substrate in order to prevent cracking.

At step 1308, the electroplated aluminum layer may be surface finished.For example, a minimum thickness of 10 um of the electroplated aluminumlayer may be too thin to polish, but may be required in order to achievea textured finish. As another example, a minimum thickness of 18 um oflayer 230 may be required to achieve a mirror finish. At step 1310, thesurface finished electroplated aluminum layer may be anodized. In someembodiments, a dye coloring process can be performed during anodizingstep 1310 in order to achieve a coloring effect.

Though not shown, in some embodiments, the electroplated aluminum layercan be deposited onto the non-cosmetic structure in separate layers. Forexample, to control the thickness of the electroplated aluminum layer, arough electroplated aluminum layer and a fine electroplated aluminumlayer may separately be deposited. The rough electroplated aluminumlayer may first be applied onto the non-cosmetic structure to serve as abase layer of aluminum, where the fine electroplated aluminum layer maybe subsequently applied on the rough layer. In some embodiments, thefine layer, rather than the rough layer, may first be applied onto thenon-cosmetic structure.

FIG. 14 is a schematic view of an illustrative electronic device 1400for displaying visible information to a user. Electronic device 1400 maybe any portable, mobile, or hand-held electronic device configured topresent visible information on a display assembly wherever the usertravels. Alternatively, electronic device 1400 may not be portable atall, but may instead be generally stationary. Electronic device 1400 caninclude, but is not limited to, a music player, video player, stillimage player, game player, other media player, music recorder, movie orvideo camera or recorder, still camera, other media recorder, radio,medical equipment, domestic appliance, transportation vehicleinstrument, musical instrument, calculator, cellular telephone, otherwireless communication device, personal digital assistant, remotecontrol, pager, computer (e.g., desktop, laptop, tablet, server, etc.),monitor, television, stereo equipment, set up box, set-top box, boombox, modem, router, keyboard, mouse, speaker, printer, and combinationsthereof. In some embodiments, electronic device 1400 may perform asingle function (e.g., a device dedicated to displaying image content)and, in other embodiments, electronic device 1400 may perform multiplefunctions (e.g., a device that displays image content, plays music, andreceives and transmits telephone calls).

Electronic device 1400 may include a housing 1401, a processor orcontrol circuitry 1402, memory 1404, communications circuitry 1406,power supply 1408, input component 1410, and display assembly 1412.Electronic device 1400 may also include a bus 1403 that may provide adata transfer path for transferring data and/or power, to, from, orbetween various other components of device 1400. In some embodiments,one or more components of electronic device 1400 may be combined oromitted. Moreover, electronic device 1400 may include other componentsnot combined or included in FIG. 14. For the sake of simplicity, onlyone of each of the components is shown in FIG. 1.

Memory 1404 may include one or more storage mediums, including forexample, a hard-drive, flash memory, permanent memory such as read-onlymemory (“ROM”), semi-permanent memory such as random access memory(“RAM”), any other suitable type of storage component, or anycombination thereof. Memory 1404 may include cache memory, which may beone or more different types of memory used for temporarily storing datafor electronic device applications. Memory 1404 may store media data(e.g., music, image, and video files), software (e.g., for implementingfunctions on device 1400), firmware, preference information (e.g., mediaplayback preferences), lifestyle information (e.g., food preferences),exercise information (e.g., information obtained by exercise monitoringequipment), transaction information (e.g., information such as creditcard information), wireless connection information (e.g., informationthat may enable device 1400 to establish a wireless connection),subscription information (e.g., information that keeps track of podcastsor television shows or other media a user subscribes to), contactinformation (e.g., telephone numbers and e-mail addresses), calendarinformation, any other suitable data, or any combination thereof.

Communications circuitry 1406 may be provided to allow device 1400 tocommunicate with one or more other electronic devices or servers usingany suitable communications protocol. For example, communicationscircuitry 1406 may support Wi-Fi™ (e.g., an 802.11 protocol), Ethernet,Bluetooth™, high frequency systems (e.g., 900 MHz, 2.4 GHz, and 5.6 GHzcommunication systems), infrared, transmission control protocol/internetprotocol (“TCP/IP”) (e.g., any of the protocols used in each of theTCP/IP layers), hypertext transfer protocol (“HTTP”), BitTorrent™, filetransfer protocol (“FTP”), real-time transport protocol (“RTP”),real-time streaming protocol (“RTSP”), secure shell protocol (“SSH”),any other communications protocol, or any combination thereof.Communications circuitry 1406 may also include circuitry that can enabledevice 1400 to be electrically coupled to another device (e.g., acomputer or an accessory device) and communicate with that other device,either wirelessly or via a wired connection.

Power supply 1408 may provide power to one or more of the components ofdevice 1400. In some embodiments, power supply 1408 can be coupled to apower grid (e.g., when device 1400 is not a portable device, such as adesktop computer). In some embodiments, power supply 1408 can includeone or more batteries for providing power (e.g., when device 1400 is aportable device, such as a cellular telephone). As another example,power supply 1408 can be configured to generate power from a naturalsource (e.g., solar power using one or more solar cells).

One or more input components 1410 may be provided to permit a user tointeract or interface with device 1400. For example, input component1410 can take a variety of forms, including, but not limited to, a trackpad, dial, click wheel, scroll wheel, touch screen, one or more buttons(e.g., a keyboard), mouse, joy stick, track ball, and combinationsthereof. For example, input component 1410 may include a multi-touchscreen. Each input component 1410 can be configured to provide one ormore dedicated control functions for making selections or issuingcommands associated with operating device 1400.

Electronic device 1400 may also include one or more output componentsthat may present information (e.g., textual, graphical, audible, and/ortactile information) to a user of device 1400. An output component ofelectronic device 1400 may take various forms, including, but notlimited, to audio speakers, headphones, audio line-outs, visualdisplays, antennas, infrared ports, rumblers, vibrators, or combinationsthereof.

For example, electronic device 1400 may include display assembly 1412 asan output component. Display 1412 may include any suitable type ofdisplay or interface for presenting visible information to a user ofdevice 1400. In some embodiments, display 1412 may include a displayembedded in device 1400 or coupled to device 1400 (e.g., a removabledisplay). Display 1412 may include, for example, a liquid crystaldisplay (“LCD”), a light emitting diode (“LED”) display, an organiclight-emitting diode (“OLED”) display, a surface-conductionelectron-emitter display (“SED”), a carbon nanotube display, ananocrystal display, any other suitable type of display, or combinationthereof. Alternatively, display 1412 can include a movable display or aprojecting system for providing a display of content on a surface remotefrom electronic device 1400, such as, for example, a video projector, ahead-up display, or a three-dimensional (e.g., holographic) display. Asanother example, display 1412 may include a digital or mechanicalviewfinder. In some embodiments, display 1412 may include a viewfinderof the type found in compact digital cameras, reflex cameras, or anyother suitable still or video camera.

It should be noted that one or more input components and one or moreoutput components may sometimes be referred to collectively as an I/Ointerface (e.g., input component 1410 and display 1412 as I/O interface1411). It should also be noted that input component 1410 and display1412 may sometimes be a single I/O component, such as a touch screenthat may receive input information through a user's touch of a displayscreen and that may also provide visual information to a user via thatsame display screen.

Processor 1402 of device 1400 may control the operation of manyfunctions and other circuitry provided by device 1400. For example,processor 1402 may receive input signals from input component 1410and/or drive output signals to display assembly 1412. Processor 1402 mayload a user interface program (e.g., a program stored in memory 1404 oranother device or server) to determine how instructions or data receivedvia an input component 1410 may manipulate the way in which informationis provided to the user via an output component (e.g., display 1412).For example, processor 1402 may control the viewing angle of the visibleinformation presented to the user by display 1412 or may otherwiseinstruct display 1412 to alter the viewing angle.

Electronic device 1400 may also be provided with a housing 1401 that mayat least partially enclose one or more of the components of device 1400for protecting them from debris and other degrading forces external todevice 1400. In some embodiments, one or more of the components may beprovided within its own housing (e.g., input component 1410 may be anindependent keyboard or mouse within its own housing that may wirelesslyor through a wire communicate with processor 1402, which may be providedwithin its own housing). All or a portion of housing 1401 can befinished, for example, to have an anodized electroplated aluminum finishaccording to embodiments of the invention.

The described embodiments of the invention are presented for the purposeof illustration and not of limitation.

What is claimed is:
 1. A support structure for an electronic device, thesupport structure comprising: a coating covering a surface of thesupport structure, the coating comprising: a first aluminum layercharacterized as having a first grain structure associated with a firsthardness quality, and a second aluminum layer adjacent the firstaluminum layer, the second aluminum layer characterized as having asecond grain structure different than the first grain structure, thesecond grain structure associated with a second hardness qualitydifferent than the first hardness quality, wherein the first grainstructure of the first aluminum layer cooperates with the second grainstructure of the second aluminum layer to impart a hardness quality tothe coating different than first hardness quality and the secondhardness quality.
 2. The support structure of claim 1, wherein the firstaluminum layer includes a first dopant associated with providing thefirst grain structure and the second aluminum layer includes a seconddopant associated with providing the second grain structure, the firstdopant different than the second dopant.
 3. The support structure ofclaim 1, wherein the first grain structure is associated with a firstgrain size and the second grain structure is associated with a secondgrain size, the first grain size larger than the second grain size. 4.The support structure of claim 1, wherein the first grain structure isassociated with a first grain size and the second grain structure isassociated with a second grain size, the first grain size smaller thanthe second grain size.
 5. The support structure of claim 1, wherein eachof the first and second layers is an electroplated layer.
 6. The supportstructure of claim 1, the support structure further comprising: aqualification layer positioned between the coating and the surface ofthe support structure.
 7. The support structure of claim 6, wherein thequalification layer enhances a bonding of the coating with the surfaceof the support structure.
 8. The support structure of claim 7, whereinthe qualification layer comprises a nickel layer.
 9. The supportstructure of claim 8, wherein the qualification layer comprises a copperlayer.
 10. The support structure of claim 9, wherein the copper layer isadjacent the surface of the support structure and the nickel layer ispositioned between the copper layer and the coating.
 11. The supportstructure of claim 1, wherein the coating has a thickness rangingbetween 15 and 120 micrometers.
 12. An electronic device, comprising: ahousing comprising a base comprising a base material, the housing havinga coating comprising: a first electroplated layer disposed on the basematerial, the first electroplated layer characterized as having a firstgrain size, and a second electroplated layer disposed on the firstelectroplated layer, the second electroplated layer characterized ashaving a second grain size different than the first grain size.
 13. Theelectronic device of claim 12, wherein the coating is a first coatingdisposed on a first section of the base material, the housing comprisinga second coating disposed on a second section of the base materialadjacent the first section such that the first coating is adjacent thesecond coating.
 14. The electronic device of claim 13, wherein the firstcoating has a greater thickness than the second coating.
 15. Theelectronic device of claim 13, wherein the first coating includes afirst oxide layer and the second coating includes a second oxide layer.16. The electronic device of claim 15, wherein the first coatingincludes a qualification layer between the base material and the firstelectroplated layer.
 17. The electronic device of claim 16, wherein atop surface of the first oxide layer corresponds to a first exteriorsurface portion of the housing and a top surface of the second oxidelayer corresponds to a second exterior surface portion of the housing.18. The electronic device of claim 13, wherein the first coating ischaracterized as having a first finish and the second coating ischaracterized as having a second finish different than the first finish.19. A coating disposed on a support structure of an electronic device,the coating comprising: a first electroplated aluminum layer having afirst grain structure, and a second electroplated aluminum layerdisposed on the first electroplated aluminum layer, the secondelectroplated aluminum layer having a second grain structure differentthan the first grain structure.
 20. The coating of claim 19, furthercomprising: a qualification layer between the support structure and thefirst electroplated layer, the qualification layer chosen to have anoptical brightness that imparts an optical quality to the coating.